Nanocomposites from fluoro‐oxygenated polyethylene: A novel route to organoclay exfoliation

We present a novel approach to improving organoclay exfoliation in a nonpolar matrix, polyethylene. High-density polyethylene (HDPE) particles were modified by exposure to a reactive gas atmosphere containing F2 and O2. This treatment was aimed at increasing the polarity of the polymer with the formation of carboxyl, hydroxy, and ketone functionalities on the particle surface. The surface-treated high-density polyethylene (ST-HDPE) particles were then melt-mixed with an appropriate organoclay to form nanocomposites. Transmission electron microscopy (TEM), wide-angle X-ray scattering, stress–strain analysis, and Izod impact measurements were used to evaluate the nanocomposite morphology and physical properties. These data were compared to those of equivalent nanocomposites prepared from unmodified HDPE and high-density polyethylene grafted with maleic anhydride (HDPE-g-MA). The nanocomposites prepared from the ST-HDPE particles exhibited much better properties and organoclay dispersion than those prepared from unmodified HDPE. The level of reinforcement observed in ST-HDPE-based nanocomposites was comparable to, if not better than, that seen in HDPE-g-MA-based nanocomposites. However, a comparison of the TEM micrographs suggested better organoclay exfoliation in HDPE-g-MA than the current version of ST-HDPE. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 2980–2989, 2006

[1]  Donald R Paul,et al.  TPO based nanocomposites. Part 1. Morphology and mechanical properties , 2005 .

[2]  R. K. Shah,et al.  Nanocomposites from poly(ethylene- co -methacrylic acid) ionomers: effect of surfactant structure on morphology and properties , 2005 .

[3]  D. R. Paul,et al.  Comparison of nanocomposites based on nylon 6 and nylon 66 , 2004 .

[4]  D. R. Paul,et al.  Nanocomposites formed from linear low density polyethylene and organoclays , 2004 .

[5]  K. Mauritz,et al.  Surlyn®/silicate nanocomposite materials via a polymer in situ sol–gel process: Morphology , 2003 .

[6]  Makoto Kato,et al.  Polyolefin-clay hybrids based on modified polyolefins and organophilic clay , 2000 .

[7]  Jeffrey W. Gilman,et al.  Flammability and thermal stability studies of polymer layered-silicate (clay) nanocomposites , 1999 .

[8]  R. Vaia,et al.  Polymer/layered silicate nanocomposites as high performance ablative materials , 1999 .

[9]  Zhu Xiaoguang,et al.  Studies on nylon 6/clay nanocomposites by melt-intercalation process , 1999 .

[10]  Thomas J. Pinnavaia,et al.  Nanolayer Reinforcement of Elastomeric Polyurethane , 1998 .

[11]  A. Okada,et al.  Preparation and mechanical properties of polypropylene-clay hybrids using a maleic anhydride-modified polypropylene oligomer , 1998 .

[12]  P. Messersmith,et al.  Synthesis and barrier properties of poly(ε‐caprolactone)‐layered silicate nanocomposites , 1995 .

[13]  Toshio Kurauchi,et al.  Interaction of nylon 6‐clay surface and mechanical properties of nylon 6‐clay hybrid , 1995 .

[14]  T. Pinnavaia,et al.  Clay-Reinforced Epoxy Nanocomposites , 1994 .

[15]  T. Kurauchi,et al.  Synthesis and properties of polyimide–clay hybrid , 1993 .