Selective Laser Melting of Prealloyed High Alloy Steel Powder Beds

This paper presents the results of a recent comprehensive investigation of selective laser melting (slm) of prealloyed gas and water atomised M2 and H13 tool steel powders. The objective of the study was to establish the parameters that control the densification of single and multiple layers with the aim of producing high density parts without the need for infiltration. Powders were processed using continuous wave (CW) CO2 and Nd:YAG lasers. Relationships between alloy composition, powder particle size and shape, flowability, microstructure (phases present, their size, morphology and distribution), track morphology, post scanned density, surface finish and scan conditions (Laser power, spot size and scan speed) are discussed for single track, single layer and multi-layer (up to 25 layers) constructions. Processing with a Nd:YAG laser with powders placed on substrates rather than on a loose powder bed gave more stable builds than with the CO2 laser. Using the Nd:YAG laser densities up to ~90% relative were possible with H13 powder compared with a maximum of ~70% for M2 in multi-layer builds. Maximum density achieved with CW CO2 processing was only ~60%, irrespective of powder composition. The paper compares the processibility of these materials with stainless steel powders processed to higher densities (up to 99% relative) under similar conditions. The results of the work show that a crucial factor for high density processing is melt pool wettability and this is controlled largely by carbon content; low carbon contents producing better wettability, flatter tracks and higher densities. The significance of this observation for the processing high alloy steels by slm will be discussed.

[1]  R. Morgan,et al.  Density analysis of direct metal laser re-melted 316L stainless steel cubic primitives , 2004 .

[2]  C. S. Wright,et al.  Processing conditions and mechanical properties of high-speed steel parts fabricated using direct selective laser sintering , 2003 .

[3]  Gideon Levy,et al.  RAPID MANUFACTURING AND RAPID TOOLING WITH LAYER MANUFACTURING (LM) TECHNOLOGIES, STATE OF THE ART AND FUTURE PERSPECTIVES , 2003 .

[4]  Olli Nyrhilä,et al.  Rapid Manufacturing with Direct Metal Laser Sintering , 2002 .

[5]  I. Chang,et al.  Selective laser sintering of gas and water atomized high speed steel powders , 1999 .

[6]  Approaches to processing metal and ceramics through laser scanning of powder beds , 2001 .

[7]  Carl Hauser,et al.  Selective laser sintering of a stainless steel powder , 2003 .

[8]  C. M. Taylor,et al.  DIRECT SELECTIVE LASER SINTERING OF TOOL STEEL POWDERS TO HIGH DENSITY. PART A: EFFECTS OF LASER BEAM WIDTH AND SCAN STRATEGY , 2003 .

[9]  Yu. V. Khlopkov,et al.  Absorptance of powder materials suitable for laser sintering , 2000 .

[10]  C. S. Wright,et al.  Supersolidus liquid phase sintering of high speed steels: Part 3: computer aided design of sinterable alloys , 1999 .

[11]  Kenny Dalgarno,et al.  Production tooling for polymer moulding using the RapidSteel process , 2001 .

[12]  I. Chang,et al.  Instability of scan tracks of selective laser sintering of high speed steel powder , 1999 .

[13]  C. S. Wright,et al.  FRACTURE BEHAVIOUR OF A HIGHLY ALLOYED HIGH SPEED STEEL , 1995 .