The effects of surface pretreatment on the cyclic-fatigue characteristics of bonded aluminium-alloy joints

The present work has used an accelerated test method, based upon cyclic-fatigue testing using a fracture-mechanics approach, to study the durability of organosilanepretreated joints which were adhesively-bonded using a hot-cured epoxy-film adhesive. The silane primer investigated was γ-glycidoxypropyltrimethoxysilane (GPS). The cyclic-fatigue tests were mainly conducted in (a) a ‘dry’ environment of 25 ± 2°C with a relative humidity of 55 ± 5% and (b) a ‘wet’ environment where the joints were fully immersed in distilled water at 28 ± 2°C. However, tests were also undertaken by varying the relative humidity of the environment. The loci of failure of the joints were identified using various surface specific techniques. The use of the GPS-pretreatment has been shown to be effective in increasing the joint durability, compared with a simple grit-blast and degrease (GBD) treatment and, indeed, gives comparable results to using a chromic-acid etch (CAE) pretreatment.

[1]  J. Watts,et al.  The Interaction of γ-Glycidoxypropyltrimethoxysilane with Oxidised Aluminium Substrates: The Effect of Drying Temperature , 2000 .

[2]  Durability of Bonds Formed Between Epoxy Adhesive and Aluminium Alloy Treated with Phosphonate Inhibitors , 1996 .

[3]  A. Kinloch,et al.  The Locus of Environmental Crack Growth in Bonded Aluminium Alloy Joints , 1984 .

[4]  G. D. Davis,et al.  Subadhesive hydration of aluminum adherends and its detection by electrochemical impedance spectroscopy , 1995 .

[5]  S. J. Shaw,et al.  A Model for Predicting Joint Durability , 1980 .

[6]  M. Gettings,et al.  Surface analysis of polysiloxane/metal oxide interfaces , 1977 .

[7]  M Martignoni,et al.  [Silane coupling agents]. , 1990, Attualita dentale.

[8]  Homayoun Hadavinia,et al.  Predicting the service-life of adhesively-bonded joints , 2000 .

[9]  E. Plueddemann,et al.  SILANE COUPLING AGENTS , 1982 .

[10]  J. G. Williams,et al.  The calculation of adhesive fracture energies in mode I: revisiting the tapered double cantilever beam (TDCB) test , 2003 .

[11]  J. S. Ahearn,et al.  Environmental durability of phosphoric acid anodized aluminium adhesive joints protected with hydration inhibitors , 1986 .

[12]  Anthony J. Kinloch,et al.  The Fatigue and Durability Behaviour of Automotive Adhesives. Part I: Fracture Mechanics Tests , 1997 .

[13]  J. D. Venables,et al.  Adhesion and durability of metal-polymer bonds , 1984 .

[14]  S. Shaw,et al.  The international collaborative programme on organosilane coupling agents: an introduction☆ , 1998 .

[15]  Anthony J. Kinloch,et al.  The role of the interphase in the environmental failure of adhesive joints , 2000 .

[16]  A. Kinloch.  Adhesion and adhesives , 1987 .

[17]  Peter G. Pape,et al.  Methods for improving the performance of silane coupling agents , 1991 .

[18]  J. Watts,et al.  Evidence of specific interaction between γ‐glycidoxypropyltrimethoxysilane and oxidized aluminium using high‐mass resolution ToF‐SIMS† , 2000 .

[19]  J. Comyn,et al.  The effect of humidity on the durability of aluminium-epoxide joints , 1990 .