Internal stress relaxation based method for elastic stiffness characterization of very thin films

Accurate measurement of the Young's modulus of films with thickness smaller than a few hundreds of nanometers remains extremely challenging. The present method disclosed here is based on the combined measurements of the internal stress using the Stoney method and of the corresponding elastic strain obtained by releasing microstructures. Experimental validation is presented for silicon nitride films. The Young's moduli of the 100, 300, and 500 nm-thick films are equal to 193 +/- 20 GPa. 226 +/- 22 GPa, and 208 +/- 18 GPa, respectively, in good agreement with nanoindentation test results. This very simple method can potentially be used for much thinner films and extended to materials involving no internal stress. (C) 2009 Elsevier B.V. All rights reserved.

[1]  R. L. Edwards,et al.  Comparison of tensile and bulge tests for thin-film silicon nitride , 2004 .

[2]  T. Pardoen,et al.  Three-Dimensional Self-Assembled Sensors in Thin-Film SOI Technology , 2006, Journal of Microelectromechanical Systems.

[3]  A. Rosakis,et al.  Thin film/substrate systems featuring arbitrary film thickness and misfit strain distributions. Part II: Experimental validation of the non-local stress/curvature relations , 2007 .

[4]  N. Chiba,et al.  Young's modulus, fracture strain, and tensile strength of sputtered titanium thin films , 2005 .

[5]  Microfabrication-based nanomechanical laboratory for testing the ductility of submicron aluminium films , 2007 .

[6]  Tong-Yi Zhang,et al.  Microbridge testing of silicon nitride thin films deposited on silicon wafers , 2000 .

[7]  Xi Chen,et al.  Numerical study on the measurement of thin film mechanical properties by means of nanoindentation , 2001 .

[8]  J. Vlassak,et al.  High-throughput analysis of thin-film stresses using arrays of micromachined cantilever beams. , 2008, The Review of scientific instruments.

[9]  G. Rehder,et al.  PECVD a-Sic:H Young’s modulus obtained by MEMS resonant frequency , 2008 .

[10]  Horacio Dante Espinosa,et al.  A methodology for determining mechanical properties of freestanding thin films and MEMS materials , 2003 .

[11]  Denis Flandre,et al.  Bulk and surface micromachined MEMS in thin film SOI technology , 2007 .

[12]  Joost J. Vlassak,et al.  A new bulge test technique for the determination of Young’s modulus and Poisson’s ratio of thin films , 1992 .

[13]  Oliver Paul,et al.  Mechanical properties of thin films from the load deflection of long clamped plates , 1998 .

[14]  Hong-ying Chen,et al.  Evaluation of Poisson's ratio and Young's modulus of nitride films by combining grazing incidence X-ray diffraction and laser curvature techniques , 2007 .

[15]  Denis Flandre,et al.  Thin films stress extraction using micromachined structures and wafer curvature measurements , 2004 .

[16]  R. Mountain,et al.  A technique for the determination of stress in thin films , 1983 .

[17]  Claude A. Klein,et al.  How accurate are Stoney’s equation and recent modifications , 2000 .

[18]  Freund.  Thin Film Materials , 2004 .

[19]  A. Boe,et al.  New On-Chip Nanomechanical Testing Laboratory - Applications to Aluminum and Polysilicon Thin Films , 2009, Journal of Microelectromechanical Systems.

[20]  G. Stoney.  The Tension of Metallic Films Deposited by Electrolysis , 1909 .

[21]  Arnaud Devos,et al.  Complete thin film mechanical characterization using picosecond ultrasonics and nanostructured transducers: experimental demonstration on SiO2 , 2008 .

[22]  M. Gaitan,et al.  Young's Modulus Measurements in Standard IC CMOS Processes Using MEMS Test Structures , 2007, IEEE Electron Device Letters.

[23]  M. P. Boer,et al.  On-chip test structure suite for free-standing metal film mechanical property testing, Part I – Analysis , 2008 .

[24]  A. Rosakis,et al.  Multilayer thin films/substrate system with variable film thickness subjected to non-uniform misfit strains , 2008 .

[25]  B.J. Gallacher,et al.  Analysis of a Passive Sensor for Predicting Process-Induced Stress in Advanced Integrated Circuit Interconnect , 2008, IEEE Transactions on Device and Materials Reliability.

[26]  D. W. Burns,et al.  Diagnostic microstructures for the measurement of intrinsic strain in thin films , 1992 .

[27]  P. Kotula,et al.  On-chip laboratory suite for testing of free-standing metal film mechanical properties, Part II -Experiments , 2008 .

[28]  Ares J. Rosakis,et al.  Thin film/substrate systems featuring arbitrary film thickness and misfit strain distributions. Part I: Analysis for obtaining film stress from non-local curvature information , 2007 .

[29]  G. Pharr,et al.  An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments , 1992 .

[30]  Michael Huth,et al.  Suppression of martensitic phase transition at the Ni2MnGa film surface , 2008 .

[31]  H. Espinosa,et al.  Design and Operation of a MEMS-Based Material Testing System for Nanomechanical Characterization , 2007, Journal of Microelectromechanical Systems.