论文信息 - STRUCTURE AND MAGNETIC PROPERTIES OF TB0.27 DY0.73FE1.9+xTI0.05 COMPOUNDS

STRUCTURE AND MAGNETIC PROPERTIES OF TB0.27 DY0.73FE1.9+xTI0.05 COMPOUNDS

Structure, Curie temperature, and magnetostriction have been systemically investigated for Tb0.27Dy0.73 Fe1.9+xTi0.05 compounds using X-ray diffraction, vibrating sample magnetometer, and standard strain gauge technique. The samples show pure MgCu2-type Laves phase when x≥0.2, and a small amount of second phases appear when x>0.2. The lattice parameters and the Curie temperatures change modestly with increasing Fe content. The magnetostriction of Tb0.27Dy0.73Fe1.9+xTi0.05 compounds shows strong dependence on Fe content.

Z. Ren | Zunming Lu | Yangxiang Li | Songtao Li | Heyan Liu

[1] Xiangxi Meng,et al. Synthesis of Iron-Based Laves Phase Containing Praseodymium Magnetostrictive Materials , 2007 .

[2] Wenzhu Liu,et al. Magnetostriction and anisotropy compensation in TbxDy1-xPr0.3(Fe0.9B0.1)(1.93) alloys , 2004 .

[3] Weili Yan,et al. Magnetostrictive and magnetic properties of the pseudobinary compounds PrxTb1−xFe2 and Pr0.15TbxDy0.85−xFe2 , 1998 .

[4] Y. Tang. Transition-metal substitution effect on magnetic and magnetostrictive properties of TbFe2 compounds , 1997 .

[5] Wu Mei,et al. Phase diagram and inhomogeneity of (TbDy)-Fe(T) (T = Mn, Co, Al, Ti) systems , 1997 .

[6] Guangheng Wu,et al. 〈111〉 oriented and twin‐free single crystals of Terfenol‐D grown by Czochralski method with cold crucible , 1995 .

[7] X. Chen,et al. The effects of boron on Tb0.27Dy0.73Fe2 compound , 1995 .