On the propagation and coalescence of delamination cracks in compressed coatings: with application to thermal barrier systems

[1]  A. Bartz,et al.  Strength Degradation and Failure Mechanisms of Electron‐Beam Physical‐Vapor‐Deposited Thermal Barrier Coatings , 2004 .

[2]  John W. Hutchinson,et al.  Simulation of stresses and delamination in a plasma-sprayed thermal barrier system upon thermal cycling , 2003 .

[3]  A. Evans,et al.  A Fundamental Model of Cyclic Instabilities in Thermal Barrier Systems , 2002 .

[4]  E. Jordan,et al.  Thermal Barrier Coatings for Gas-Turbine Engine Applications , 2002, Science.

[5]  A. G. Evans,et al.  Characterization of a cyclic displacement instability for a thermally grown oxide in a thermal barrier system , 2001 .

[6]  Anette M. Karlsson,et al.  A numerical model for the cyclic instability of thermally grown oxides in thermal barrier systems , 2001 .

[7]  Jianguo Lin,et al.  A mechanistic study of oxidation-induced degradation in a plasma-sprayed thermal barrier coating system.: Part II: Life prediction model , 2001 .

[8]  Robert Vaßen,et al.  Development of a micromechanical life prediction model for plasma sprayed thermal barrier coatings , 2001 .

[9]  M. Nakayama,et al.  A MECHANISTIC STUDY OF OXIDATION-INDUCED DEGRADATION IN A PLASMA-SPRAYED THERMAL BARRIER COATING SYSTEM. PART I: MODEL FORMULATION , 2001 .

[10]  Jack Beuth,et al.  Measurement of interfacial toughness in thermal barrier coating systems by indentation , 2001 .

[11]  Anthony G. Evans,et al.  Mechanisms controlling the durability of thermal barrier coatings , 2001 .

[12]  E. Tzimas,et al.  Failure of thermal barrier coating systems under cyclic thermomechanical loading , 2000 .

[13]  A. G. Evans,et al.  Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings , 2000 .

[14]  David R. Clarke,et al.  Surface rumpling of a (Ni, Pt)Al bond coat induced by cyclic oxidation , 2000 .

[15]  Hiroshi Tada,et al.  The stress analysis of cracks handbook , 2000 .

[16]  A. Evans,et al.  Micromechanics model for the detachment of residually compressed brittle films and coatings , 1999 .

[17]  E. Jordan,et al.  Mechanism of spallation in platinum aluminide/electron beam physical vapor-deposited thermal barrier coatings , 1999 .

[18]  F. Pettit,et al.  Thermal Barrier Coatings for the 21st Century , 1999, International Journal of Materials Research.

[19]  A. Evans,et al.  Effect of interface undulations on the thermal fatigue of thin films and scales on metal substrates , 1997 .

[20]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[21]  Robert A. Miller,et al.  Oxidation‐Based Model for Thermal Barrier Coating Life , 1984 .